Weld Mold® 601


A cobalt base wear-facing alloy designed for maximum abrasion and corrosion resistance. Provides excellent metal to metal wear, oxidation and high stress abrasion wear at high temperatures and in corrosive environments. Maintains an effective hardness at operating temperature up to 1800º F.

Applications

Primarily employed as a hard overlay on parts subject to abrasion and corrosive media. Used for wear facing cement plant machinery, agricultural machinery, iron and steel plant equipment, metal working tools, coke pusher shoes, and carbon scrapers.

Procedure

Remove all foreign material, fatigued metal, and any sharp radii. On mild steels a pre-heat of 350°F is recommended. On higher alloy steels you must pre-heat according to base metal composition, the type of weld, and the amount of deposit. Low alloy steels may be put into service in the as-welded condition. Heat treatable steels should be tempered at 1000º F for 4 to 6 hours then cooled in still air.

SMAW - DC+
FCAW - DC+, 75% Ar 25% CO2 or 100% CO2
GTAW - DC- 100% Ar